LEXAN(沙伯基礎)LS1/PC(聚碳酸酯)_價格_物性_圖片_UL黃卡

Material Notes:

LEXAN LS1 is a low viscosity injection moulding grade especially designed for manufacturing complex parts requiring easy flow properties combined with high optical requirements.

Density密度 

1.20 g/cc

0.0434 lb/in3

ISO 1183

Moisture Absorption at Equilibrium吸濕平衡 

0.15 %

0.15 %

23°C / 50% RH; ISO 62

Water Absorption at Saturation吸水率 

0.35 %
@Temperature 23.0 °C

0.35 %
@Temperature 73.4 °F

ISO 62

Linear Mold Shrinkage, Flow線性收縮率/流動 

0.0050 - 0.0070 cm/cm

0.0050 - 0.0070 in/in

on tensile bar; SABIC Method

Melt Flow熔體流動速率 

21 g/10 min
@Load 1.20 kg,
Temperature 300 °C

21 g/10 min
@Load 2.65 lb,
Temperature 572 °F

[cm^3/10 min] Melt Volume Rate; ISO 1133

Mechanical Properties力學性能

Metric公制數據

English英制數據

Comments測試方法

Hardness,硬度 H358/30 

95.0 MPa

13800 psi

ISO 2039-1

Tensile Strength at Break斷裂拉伸強度 

70.0 MPa

10200 psi

50 mm/min; ISO 527

Tensile Strength, Yield屈服拉伸強度 

63.0 MPa

9140 psi

50 mm/min; ISO 527

Elongation at Break斷裂伸長率 

100 %

100 %

50 mm/min; ISO 527

Elongation at Yield屈服伸長率 

6.0 %

6.0 %

50 mm/min; ISO 527

Tensile Modulus拉伸模量 

2.35 GPa

341 ksi

1 mm/min; ISO 527

Flexural Yield Strength彎曲屈服強度 

90.0 MPa

13100 psi

2 mm/min; ISO 178

Flexural Modulus彎曲彈性模量 

2.30 GPa

334 ksi

2 mm/min; ISO 178

Izod Impact, Notched懸臂梁缺口沖擊強度 (ISO)  

11.0 kJ/m2
@Temperature -30.0 °C

5.23 ft-lb/in2
@Temperature -22.0 °F

80*10*3; ISO 180/1A

65.0 kJ/m2
@Temperature 23.0 °C

30.9 ft-lb/in2
@Temperature 73.4 °F

80*10*3; ISO 180/1A

Izod Impact, Unnotched懸臂梁無缺口沖擊強度 (ISO) 

NB
@Temperature 23.0 °C

NB
@Temperature 73.4 °F

80*10*3; ISO 180/1U

NB
@Temperature -30.0 °C

NB
@Temperature -22.0 °F

80*10*3; ISO 180/1U

Charpy Impact Unnotched夏比缺口試樣沖擊 

NB
@Temperature 23.0 °C

NB
@Temperature 73.4 °F

Edgew 80*10*3 sp=62mm; ISO 179/1eU

NB
@Temperature -30.0 °C

NB
@Temperature -22.0 °F

Edgew 80*10*3 sp=62mm; ISO 179/1eU

Charpy Impact, Notched夏比缺口沖擊 

1.20 J/cm2
@Temperature -30.0 °C

5.71 ft-lb/in2
@Temperature -22.0 °F

V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA

6.50 J/cm2
@Temperature 23.0 °C

30.9 ft-lb/in2
@Temperature 73.4 °F

V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA

Taber Abrasion, mg/1000 Cycles周期泰伯磨耗 

10
@Load 1.00 kg

10
@Load 2.20 lb

CS-17; SABIC Method

Electrical Properties電性能

Metric公制數據

English英制數據

Comments測試方法

Volume ResiSTivity體積電阻率 

>= 1.00e+15 ohm-cm

>= 1.00e+15 ohm-cm

IEC 60093

Surface Resistance表面電阻 

>= 1.00e+15 ohm

>= 1.00e+15 ohm

ROA; IEC 60093

Dielectric Constant介電常數 

2.7
@Frequency 1.00e+6 Hz

2.7
@Frequency 1.00e+6 Hz

IEC 60250

2.7
@Frequency 50.0 - 60.0 Hz

2.7
@Frequency 50.0 - 60.0 Hz

IEC 60250

Dielectric Strength介電強度 

17.0 kV/mm
@Thickness 3.20 mm

432 kV/in
@Thickness 0.126 in

in oil; IEC 60243-1

Dissipation Factor耗散因數 

0.0010
@Frequency 50.0 - 60.0 Hz

0.0010
@Frequency 50.0 - 60.0 Hz

IEC 60250

0.010
@Frequency 1.00e+6 Hz

0.010
@Frequency 1.00e+6 Hz

IEC 60250

Thermal Properties熱性能

Metric公制數據

English英制數據

Comments測試方法

CTE, linear, Parallel to Flow線性熱膨脹系數 

70.0 μm/m-°C
@Temperature 23.0 - 80.0 °C

38.9 μin/in-°F
@Temperature 73.4 - 176 °F

ISO 11359-2

Thermal Conductivity導熱系數 

0.200 W/m-K

1.39 BTU-in/hr-ft2-°F

ISO 8302

Deflection Temperature at熱變形溫度 0.46 MPa (66 psi) 

133 °C

271 °F

Edgew 120*10*4 sp=100mm; ISO 75/Be

Deflection Temperature at熱變形溫度 1.8 MPa (264 psi) 

122 °C

252 °F

Edgew 120*10*4 sp=100mm; ISO 75/Ae

Vicat Softening Point維卡軟化點 

140 °C

284 °F

Rate B/50; ISO 306

141 °C

286 °F

Rate B/120; ISO 306

UL RTI, Electrical 相對溫度指數

130 °C

266 °F

UL 746B

UL RTI, Mechanical with Impact 機械沖擊熱指數

125 °C

257 °F

UL 746B

UL RTI, Mechanical without Impact 無機械沖擊熱指數

125 °C

257 °F

UL 746B

Flammability, UL94阻燃等級  

HB
@Thickness 0.750 mm

HB
@Thickness 0.0295 in

UL 94

HB
@Thickness 3.00 mm

HB
@Thickness 0.118 in

2nd value; UL 94

Oxygen Index氧指數 

25 %

25 %

LOI; ISO 4589

Glow Wire Test灼熱絲測試 

850 °C
@Thickness 1.00 mm

1560 °F
@Thickness 0.0394 in

Glow Wire Flammability Index; IEC 60695-2-12

Optical Properties光學性質

Metric公制數據

English英制數據

Comments測試方法

ReFRactive Index折射率 

1.586

1.586

ISO 489

Haze霧度 

<= 0.80 %
@Thickness 2.54 mm

<= 0.80 %
@Thickness 0.100 in

ASTM D 1003

TRansmission, Visible透光率 

88 - 90 %
@Thickness 2.54 mm

88 - 90 %
@Thickness 0.100 in

ASTM D 1003