導讀：德國朗盛LANXESS Durethan PA6 BG30XW1是一種加30%玻璃/玻璃球，注塑成型，不易翹曲，低溫穩定的尼龍6樹脂.
德國朗盛LANXESS Durethan PA6 BG30XW1是一種加30%玻璃/玻璃球，注塑成型，不易翹曲，低溫穩定尼龍6樹脂，尼龍從環境中吸收潮氣的能力也不同。這與增塑劑的效果相同，即可以提高材料的斷裂伸長及韌性，但降低了材料的強度和剛度,除了自然色及黑色外，還可以提供一系列的不透明標準顏色；如有需要，也可以提供特定顏色的產品。
生產商：LANXESS(德國朗盛)、品名：Durethan
PA6(尼龍6)BG30XW1/德國朗盛/物性表參數
| These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350. |
| Property | Test Condition | Unit | Standard | |||
| d.a.m. | cond. | |||||
| Rheological properties | ||||||
| Molding shrinkage, parallel | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.5 | ||
| Molding shrinkage, transverse | 60x60x2; 280 °C / MT 80 °C; 600 bar | % | ISO 294-4 | 0.7 | ||
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.1 | ||
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | ISO 294-4 | 0.2 | ||
Mechanical properties (23 °C/50 % r. h.) | ||||||
| Tensile modulus | 1 mm/min | MPa | ISO 527-1,-2 | 6400 | 3200 | |
| Tensile Stress at break | 5 mm/min | MPa | ISO 527-1,-2 | 125 | 65 | |
| Tensile Strain at break | 5 mm/min | % | ISO 527-1,-2 | 4 | 10 | |
| Charpy impact strength | 23 °C | kJ/m2 | ISO 179-1eU | 45 | 75 | |
| Charpy impact strength | -30 °C | kJ/m2 | ISO 179-1eU | 40 | 45 | |
| Charpy notched impact strength | 23 °C | kJ/m2 | ISO 179-1eA | <10 | 10 | |
| Charpy notched impact strength | -30 °C | kJ/m2 | ISO 179-1eA | <10 | <10 | |
| Izod impact strength | 23 °C | kJ/m2 | ISO 180-1U | 35 | 80 | |
| Izod impact strength | -30 °C | kJ/m2 | ISO 180-1U | 30 | 40 | |
| Izod notched impact strength | 23 °C | kJ/m2 | ISO 180-1A | <10 | <10 | |
| Izod notched impact strength | -30 °C | kJ/m2 | ISO 180-1A | <10 | <10 | |
| Flexural modulus | 2 mm/min | MPa | ISO 178-A | 5800 | 2800 | |
| Flexural strength | 2 mm/min | MPa | ISO 178-A | 185 | 100 | |
| Flexural strain at flexural strength | 2 mm/min | % | ISO 178-A | 5.0 | 8.0 | |
| Flexural stress at 3.5 % strain | 2 mm/min | MPa | ISO 178-A | 175 | 80 | |
| Puncture maximum force | 23 °C | N | ISO 6603-2 | 700 | 1540 | |
| Puncture maximum force | -30 °C | N | ISO 6603-2 | 690 | 780 | |
| Puncture energy | 23 °C | J | ISO 6603-2 | 2 | 2.8 | |
| Puncture energy | -30 °C | J | ISO 6603-2 | 1.7 | 2 | |
| Ball indentation hardness | N/mm2 | ISO 2039-1 | 185 | 75 | ||